Potting compound
Non-hardening cooling potting compound
TU 2513-006-12568007-97
It is used for the potting of top and low forward wardrobe's slats and wire's exit in refrigeration.
Potting compound is a non-hardening material made from synthetic rubbers, fillers, plastifiers and additions.
Physicomechanical indexes
| Index name | TU norm |
| Exterior | Light tone without ectogenic inserts and lumps |
Ultimate strength at the tension, kgs/sq.sm., not less than
- at the temperature of (23±5) deg.C.
- at the temperature of minus (40±2) deg.C |
0,4
0,4 |
| Character of fracture | cohesive |
| Leakage resistance, mm | 0 |
| Penetration, mm, not less than | 4.0 - 8.0 |
Potting compound is packed into braids: length - 540 mm (diameter - 5 mm) [order], length 500 mm (diameter - 15 mm) [order]. Braids' potting compound is packed in series. Quantity of stratums must not be more than 15 in height.
GUAZ - obturative anticorrosive auto potting compound
TU 5770-085-00284718-95
You can use it to obdurate metallic surfaces of welds and other metallic bridgings, components, nodes and cabins of automobiles.
Potting compound is a non-hardening material made from synthetic rubbers (butyl rubber, ethylene propylene), fillers, plastifiers and technological additions.
Physicomechanical indexes
| Index name | TU norm |
|---|
| Exterior |
Soft homogeneous material from light-grey to brown color |
| Ultimate strength at the tension, kgs/sq.sm., not less than |
| - at the temperature of (23±5) deg.C. | 0.5 |
| - at the temperature of minus (60±2) deg.C Ñ | 0.5 |
| Character of fracture | cohesive |
| Leakage resistance, mm | Without refluxing |
| Penetration, mm, not less than | 8.0 |
| Dencity, kg/cub.m., not more than | 1600 |
| Impact of varish-painted coat at the temperature 140 deg. Ñ during 60 min. |
Without refluxing, inflation, cratering and change of enamel color. |
Potting compound keeps their physicomechanical properties at the temperature from - 60 to 200 deg. C. It also does not flake, evoke contraction, moreover it does not slake after finishing technological cycle (precoating, coloring, drying).
It is manufactured in briquettes (length - not more than 450 mm; mass - 1,5-3 kg). Briquette is wrapped up by thin stratum of talcum and stacked in cardboard boxes or wooden drawers.
Hygienic certificate ¹ 73.ÎÖ.11.240Ï.00013.Ñ.98.1888945 given by CGSES of Ulyanovsk region in 28.08.1998. Term operation - from 28.08.1998 until 30.08.2001
[order]
Non-hardening sealing building mastic
GOST 14791-79
You can use it to seal closed and drained butts of exterior walls and to obdurate places where window and door blocks link with wall elements.
 | It was awarded the diploma of All-Russian competition "the best 100 products of Russia"
Other awards of the plant |
Mastic is a non-hardening material made from synthetic rubbers (butyl rubber, ethylene propylene), fillers, plastifiers and additions.
Physicomechanical indexes
0.4
7 - 11
2.0
7.0
| Index name |
TU norm |
| Exterior |
Soft homogeneous material |
| Ultimate strength at the tension, kgs/sq.sm., not less than |
0.08 - 0.10 |
| Relative protraction at the maximum loading, %, not less than |
35 |
| Character of fracture |
cohesive |
| Water uptake, %, not more than |
0.4 |
| Consistence, mm |
7 - 11 |
| Refluxing of mastic at the temperature 70 deg.Ñ (heat resistance), mm, not more than |
2.0 |
| Relative protraction at the temperature minus 50 deg.Ñ, %, not less than |
7.0 |
| Migration of plastifier |
Does not admit |
You can use non-hardening mastic to seal closed and drained butts of exterior walls and to obdurate places where window and door blocks link with wall elements. In this case, mastic keeps properties at the temperature from minus 50 to plus 70 deg. C, under following conditions: width of sealing butt varies from 10 to 30 mm and relative deformation of non-hardening mastic in the weld is not more than 10%.
We manufacture mastic as braids (diameter - 50 mm, length - from 450 mm, mass - not more than 3 kg)
Briquettes are wrapped up with polyethylene pellicle, packed in boxes.
Quality certificate N ÐÎÑÑ.RU.XÏ14.ÂÎÎ481 given by "Ruscertificate" Center in 19.10.98. Term operation - from 19.10.98 until 01.10.2001.
[order]
|